Abstract:
This research is to analyze the effect of mechanical milling on the microstructure and
mechanical properties of copper-iron. The sample is fabricated by compacting, milling and sintering
processes. Sintering process is carried out using continuous type machine with conveyor belt mesh
and the furnace type is muffle. After that, it is cooled with natural water jacket process. Vicker
hardness testing and tensile strength test is performed to determine the mechanical properties of
copper-iron alloys that occur. The mean value of sample 1 hardness (before milling) was 39.8 HV.
The mean value of sample hardness 2 (after milling) was 74.9 HV. The value of the yield strength (σ)
of sample 1 is 17.597MPa, and the value of ductility (ε) is 0.119. The value of the yield strength (σ) of
sample 2 is 18.547 MPa, and the value of ductility (ε) is 0.073. The test results and analysis showed
that by shrinking the size of metal powder, by milling for 2 hours, the hardness and yield strength of
the product can increase. Although, the product becomes more brittle which is indicated by the
decreased ductility value.